Steel Treatment and Casting Ladle Bricks And Monolithic
Grade and Zone | MgO % |
SiO2 % |
CaO % |
Fe2O3 % |
Al2O3 % |
TiO2 % |
C % |
BD g/cc |
AP Vol % |
CCS N/mm2 |
---|---|---|---|---|---|---|---|---|---|---|
Working Lining | ||||||||||
Slag Line | ||||||||||
iCARB-MF9-C12-A3 | 81.25 | 0.45 | 0.93 | 0.48 | 4.89 | - | 12 | 3.00 | 3.0 | 50 |
iCARB-MF7-C12-AS7 | 80.64 | 2.37 | 1.1 | 0.54 | 3.34 | - | 12 | 2.98 | 3.3 | 45 |
iCARB-MF7-C12-A3 | 80.84 | 0.60 | 1.1 | 0.54 | 4.92 | - | 12 | 2.98 | 3.3 | 45 |
iCARB-MF1D5-C14 | 82.90 | 0.85 | 1.60 | 0.50 | 0.65 | - | 13.5 | 3.04 | 3.5 | 50 |
iCARB-MF8-C12-D | 85.33 | 0.61 | 1.10 | 0.55 | 0.41 | - | 12.0 | 3.04 | 2.7 | 50 |
Metal Line And Bottom | ||||||||||
iCARB-MF7-C07 | 90.43 | 0.61 | 1.21 | 0.59 | 0.16 | - | 7.0 | 3.09 | 3.55 | 50 |
iCARB-MF7-C07-A3 | 85.58 | 0.57 | 1.15 | 0.56 | 5.14 | - | 7.0 | 3.09 | 3.60 | 50 |
iCARB-MF7-C07-A3-C | 85.58 | 0.57 | 1.15 | 0.56 | 5.14 | - | 7.0 | 3.09 | 3.60 | 50 |
iCARB-MF5-C07-AS7 | 84.94 | 2.59 | 1.33 | 0.63 | 3.51 | - | 7.0 | 3.09 | 3.8 | 50 |
iCARB-MF9-C07-A3 | 86.08 | 0.42 | 0.96 | 0.49 | 5.05 | - | 7.0 | 3.09 | 3.5 | 60 |
iCARB-AM3-M20-C07-AS4 | 19.74 | 2.29 | 0.39 | 0.38 | 68.53 | 1.67 | 7.0 | 3.00 | 5.1 | 65 |
iCARB-AM1-M20-C07-AS4 | 19.73 | 5.14 | 0.35 | 1.17 | 64.07 | 2.54 | 7.0 | 2.88 | 6.3 | 60 |
iCARB-AM2-M09-C07C | 8.72 | 1.27 | 0.87 | 0.74 | 81.2 | - | 7.2 | 3.2 | 5.5 | 65.5 |
iCARB-AM5-M07-C07-AS1C | 6.8 | 1.25 | 0.87 | 0.25 | 83.83 | - | 7.0 | 3.20 | 4.9 | 74 |
iCARB-MF5-C07 | 86.8 | 0.66 | 1.3 | 0.5 | 0.65 | - | 7.5 | 3.14 | 3.2 | 60 |
iCARB-MF5-C10 | 87.82 | 0.68 | 1.35 | 0.2 | 0.45 | - | 9.5 | 3.08 | 3.2 | 55 |
iCARB-MF7-C10 | 87.2 | 0.64 | 1.19 | 0.58 | 0.39 | - | 10.0 | 3.05 | 3.4 | 50 |
iCARB-MF5-C14 | 83.78 | 0.72 | 1.4 | 0.15 | 0.45 | - | 13.5 | 3.06 | 3.0 | 50 |
Grade and Zone | MgO % |
SiO2 % |
CaO % |
Fe2O3 % |
Al2O3 % |
TiO2 % |
BD g/cc |
AP Vol % |
CCS N/mm2 |
PLC 1500°C 2Hrs % |
---|---|---|---|---|---|---|---|---|---|---|
Permanent Lining | ||||||||||
iFIRED-M-93. | 93.5 | 3.2 | 2.1 | 0.9 | 0.3 | - | 2.96 | 16.5 | 65 | - |
iFIRED-M-90. | 91.0 | 4.5 | 2.7 | 1.1 | 0.7 | - | 2.95 | 18.0 | 60 | - |
iFired-B-80. | 0.2 | 13.5 | 0.2 | 1.98 | 80.5 | 3.25 | 2.73 | 21 | 60 | +0.1 to -0.4 |
Monolithics | MgO % |
SiO2 % |
CaO % |
Fe2O3 % |
Al2O3 % |
TiO2 % |
P2O5 % |
BD g/cc |
CCS N/mm2 |
Particle Size mm |
---|---|---|---|---|---|---|---|---|---|---|
iGUN-M93-BX-A | 92.80 | 1.60 | 1.70 | 1.00 | 0.40 | - | - | 2.25 | 2.0 | 0-5 |
iGUN-M89-CY-PS | 89.0 | 2.6 | 2.8 | 1.0 | 0.6 | - | - | 2.20 | 2.0 | 0-5 |
iGUN M84 | 85.1 | 3.6 | 8.0 | 0.5 | 0.1 | - | 2.7 | 2.2 | 2.2 | 0-3 |
iCRETE-BA85-CA-SS | 0.3 | 8.8 | 1.4 | 1.3 | 85.1 | 2.4 | - | 2.90 | 85 | 0-10 |
iFILL-ML66-BX-P | 66.0 | 1.0 | 15.0 | 0.8 | 0.5 | - | - | 2.10 | - | 0-1 |
iFILL-ML60-BX-P | 61.0 | 1.4 | 15.5 | 1.0 | 0.8 | - | - | 2.0 | - | 0-1 |
iCAST-90(Patch) | - | 4.4 | 3.8 | 0.9 | 88 | - | - | 2.85 | 45.0 | 0-6 |
iCAST-95H-RAM | - | 0.3 | 4.5 | 0.1 | 95 | - | - | 2.90 | 70.0 | 0-6 |
iMORTAR-M95 | 95.0 | 1.60 | 1.80 | 1.10 | 0.5 | - | - | 1.37 | - | 0-1 |
iMORTAR-M85-S | 85.0 | 6.3 | 1.8 | 1.1 | 0.5 | - | - | 1.3 | - | 0-1 |
iMORTAR-B80-CY-P | 0.5 | 10.0 | 1.0 | 2.0 | 80.5 | 2.5 | 2.5 | 1.4 | - | 0-1 |
Well Blocks and PP seating blocks Pre-cast |
MgO % |
SiO2 % |
CaO % |
Fe2O3 % |
Al2O3 % |
TiO2 % |
P2O5 % |
BD g/cc |
CCS N/mm2 |
Particle Size mm |
---|---|---|---|---|---|---|---|---|---|---|
iCAST-ASP92-CA | 5.0 | - | 2.2 | 0.1 | 92 | - | - | 3.00 | - | 0-10 |
iCAST-96-CA | - | 0.2 | 3.0 | 0.1 | 96 | - | - | 2.97 | - | 0-6 |